Process for manufacturing high to ultra high molecular weight polymers using novel bridged metallocene catalysts

ABSTRACT

The present invention relates to a process of manufacturing high, very high, and ultra high molecular weight polymers comprising predominantly ethylene monomers. Ethylene is reacted in the presence of a catalyst system to produce a polymer having a viscosimetrically-determined molecular weight of at least 0.7×10 6  g/mol. The catalyst system generally includes a bridged metallocene catalyst compound, optionally with a co-catalyst. The catalyst is characterized by a zirconium dichloride central functionality and a dimethyl silandiyl bridge between five-membered rings of indenyl groups. Both rings of the metallocene compound are substituted at the 2-position with respect to the dimethyl silandiyl bridge with a C 1 -C 20  carbonaceous group.

CLAIM FOR PRIORITY

This Non-Provisional patent application is a continuation-in-part of U.S. patent application Ser. No. 11/592,538, now U.S. Pat. No. 7,598,329, entitled “Process for Manufacturing Ultra High Molecular Weight Polymers Using Novel Bridged Metallocene Catalysts”, filed on Nov. 3, 2006, the priority of which is claimed, and the disclosure of which is incorporated by reference. This application is based on German Patent Application No. DE 10 2005 052654.3, filed Nov. 4, 2005, and also U.S. Provisional Patent Application No. 60/735,438, filed in the German language on Nov. 10, 2005, the priorities of which are hereby claimed. Both documents are incorporated into this application in their entireties by reference. An English language translation of the '438 U.S. Provisional Application was filed on May 26, 2006, the entirety of which is also incorporated herein by reference.

TECHNICAL FIELD

The invention relates to a process of manufacturing high to ultra high molecular weight polymers via the polymerization and co-polymerization of olefins using catalysts and their catalyst systems.

BACKGROUND OF THE INVENTION

Ultra high molecular weight ethylene polymers refer to those having a viscosimetrically determined molecular weight of greater than 1×10⁶ g/mol. Because of their extraordinary properties, such as higher abrasion resistance and low sliding friction, such polymers have a multitude of uses. Consequently, they are used in materials handling, bulk materials handling, as well as in medical applications such as joint sockets in prosthetic joints.

High and very high molecular weight ethylene polymers refer to those having a viscosimetrically determined molecular weight of greater than that of a conventional high-density polyethylene, for example, greater than about 400,000 g/mol, and less than that of an ultra high molecular weight polyethylene. Such polymers have good impact strength and abrasion resistance, although somewhat lower than that of ultra high molecular weight ethylene polymers. They are melt processible and are used, for example, in food handling cutting boards and ortheses.

Because of these novel properties, the processing of high to ultra high molecular weight polyethylene is highly complex. Ram-extrusion and compression molding of powdered raw materials are processes used to produce molded parts, whereby the molded parts manufactured often still exhibit the characteristics of the raw powder. Films and fibers are produced using solution or gel processes, which require large amounts of solvents. An objective is therefore to develop new high to ultra high molecular weight polyethylenes, which have improved processability.

According to the present state of technology, ultra high molecular weight polyethylene is manufactured according to the low pressure process using heterogeneous Ziegler catalysts. Such catalysts are, for example, described in the following patent documents: EP186995, DE3833445, EP575840 and U.S. Pat. No. 6,559,249.

Other known catalysts for olefin polymerization are single site catalysts. According to the present state of technology, ultra high molecular weight polymers are manufactured using these catalysts only in exceptional cases and under economically unprofitable conditions. Consequently, heterogeneous constrained-geometry catalysts form ultra high molecular weight polyethylene only with moderate activity and increased long chain branching, which can lead to reduced hardness and worse abrasion properties. With so-called phenoxy-imine catalysts, UHMWPE is obtained only at low activity at economically unprofitable temperature levels. Examples of these as well as other metallocenes are described in WO9719959, WO0155231, Adv. Synth. Catal 2002, 344, 477-493, EP0798306, as well as in EP0643078.

While some bridged metallocene catalysts are known, the catalysts have not been taught in a heterogeneous polymerization process in such a way as to achieve high to ultra high molecular weight in production of ethylene homopolymers and copolymers comprising predominantly ethylene monomers. Examples of such catalysts are described in U.S. Pat. Nos. 6,417,302; 7,005,398; 7,109,278; and 7,169,864.

Surprisingly, bridged single site catalysts with a suitable ligand structure were found in connection with the present invention, which when optionally used with aluminoxanes as co-catalysts, not only permitted the manufacture of ultra high molecular weight polyethylenes with a viscosimetrically determined molecular weight of at least about 0.7×10⁶ g/mol, but also produced products with improved processability. The reason for the improved processability, without being bound to a theory, has to do with the narrower molecular weight distribution Mw/Mn of 2 to 6 compared to polymers that were manufactured using Ziegler catalysts and have a molecular weight distribution Mw/Mn of 3 to 30.

SUMMARY OF THE INVENTION

According to one aspect of the present invention, there is provided a novel process for manufacturing high, very high, and ultra high molecular weight polymers comprising predominantly ethylene monomers. The process comprises reacting ethylene, and optionally other olefin monomers, in the presence of a catalyst system which includes bridged metallocene catalysts of the type having the following general formula:

whereby:

-   -   M¹ is a transition metal of the 4^(th) to 6^(th) group of the         periodic table, whose oxidation level does not equal zero, and         is preferably Ti, Zr, Hf, V, Mo, Cr and Nb;     -   R¹ is hydrogen or a C₁-C₂₀-carbonaceous group or a halogen atom;     -   R² is hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom;     -   R³ and R¹⁰ are each identical or different and are each a C₁-C₂₀         carbonaceous group;     -   R⁴, R⁵, R⁶, R⁷, R⁸, R¹¹, R¹², R¹³, R¹⁴, and R¹⁵ are each         identical or different and are each hydrogen or a halogen atom         or a C₁-C₂₀ carbonaceous group, whereby, optionally, two or more         consecutively form a cyclic system, and preferably at least one         includes a cyclic group; and     -   R⁹ is a bridge between the ligands, which is represented by one         of the following formulas:

whereby:

-   -   M² is either silicon, germanium or tin; and     -   R¹⁶ and R¹⁷ are each identical or different and equal to         hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom.

The catalyst system optionally includes a co-catalyst. The process produces a polymer having a viscosimetrically-determined molecular weight of 0.7×10⁶ g/mol or greater.

The process according to the invention contradicts the prejudice that the economical manufacture of ultra high molecular weight polymers is impossible using aluminoxanes as co-catalysts. Through the novel ligand structure of the inventions, the catalyst is believed to be sterically shielded enough against the primary mechanism for low molecular weight products to result, namely the chain transfer to aluminoxane, without however losing its economically necessary activity to the monomers. Still further features and advantages of the invention are apparent from the following description and claims.

DETAILED DESCRIPTION OF THE INVENTION

The invention is described in detail below with reference to several embodiments and numerous examples. Such discussion is for purposes of illustration only. Modifications to particular examples within the spirit and scope of the present invention, set forth in the appended claims, will be readily apparent to one of skill in the art. Terminology used herein is given its ordinary meaning consistent with the exemplary definitions set forth immediately below.

As used herein, the term “heterogenization”, and like terms, refers to activation of a catalyst with a co-catalyst and deposition on a support. This is also referred to herein as production of a supported catalyst.

In the present invention, a C₁-C₂₀ carbonaceous group is understood to be preferably the radicals:

-   -   C₁-C₂₀ alkyl, in particular methyl, ethyl, n-propyl, i-propyl,         n-butyl, i-butyl, s-butyl, t-butyl, n-pentyl, s-pentyl,         cyclopentyl, n-hexyl, cyclohexyl, n-octyl, or cyclooctyl;     -   C₂-C₂₀ alkenyl, in particular ethenyl, propenyl, butenyl,         pentenyl, cyclopentenyl, hexenyl, cyclohexenyl, octenyl or         cyclooctenyl;     -   C₂-C₂₀ alkinyl, in particular ethynyl, propynyl, butynyl,         pentynyl, hexynyl or octynyl;     -   C₆-C₂₀ aryl, in particular benzylidene, o-methoxybenzylidene,         2,6-dimethylbenzylidene, phenyl, biphenyl, naphthyl,         anthracenyl, triphenylenyl, [1,1′,3′, 1″]-terphenyl-2′-yl,         binaphthyl, or phenanthrenyl;     -   C₁-C₂₀ fluoroalkyl, in particular trifluoromethyl,         pentafluoroethyl, 2,2,2-trifluoroethyl, 3-trifluoropropyl, or         2,2′-trifluoroisopropyl;     -   C₆-C₂₀ fluoroaryl, in particular pentafluorophenyl,         3,5-bistrifluoromethylphenyl, pentafluorobenzylidene,         3,5-bistrifluoromethylbenzylidene, tetrafluorophenyl, or         heptafluoronaphthyl;     -   C₁-C₂₀ alkoxy, in particular methoxy, ethoxy, n-propoxy,         i-propoxy, n-butoxy, i-butoxy, s-butoxy, or t-butoxy;     -   C₆-C₂₀ aryloxy, in particular phenoxy, naphthoxy, biphenyloxy,         anthracenyloxy, or phenanthrenyloxy;     -   C₇-C₂₀ arylalkyl, in particular o-tolyl, m-tolyl, p-tolyl,         2,6-dimethylphenyl, 2,6-diethylphenyl, 2,6-di-1-propylphenyl,         2,6-di-t-butylphenyl, o-t-butylphenyl, m-t-butylphenyl, or         p-t-butylphenyl;     -   C₇-C₂₀ alkylaryl, in particular benzyl, ethylphenyl,         propylphenyl, diphenylmethyl, triphenylmethyl, or methyl         naphthalene;     -   C₇-C₂₀ aryloxyalkyl, in particular o-methoxyphenyl,         m-methoxyphenyl, or p-methoxyphenyl;     -   C₁₂-C₂₀ aryloxyaryl, in particular p-phenoxyphenyl;     -   C₅-C₂₀ heteroaryl, in particular 2-pyridyl, 3-pyridyl,         4-pyridyl, chinolinyl, isochinolinyl, acridinyl,         benzochinolinyl, or benzoisochinolinyl;     -   C₄-C₂₀ heterocycloalkyl, in particular furyl, benzofuryl,         2-pyrrolidinyl, 2-indolyl, 3-indolyl, or 2,3-dihydroindolyl;     -   C₈-C₂₀ arylalkenyl, in particular o-vinylphenyl, m-vinylphenyl,         or p-vinylphenyl;     -   C₈-C₂₀ arylalkinyl, in particular o-ethynylphenyl,         m-ethynylphenyl, or p-ethynylphenyl;     -   C₁-C₂₀ heteroatomic group, in particular carbonyl, benzoyl,         oxybenzoyl, benzoyloxy, acetyl, acetoxy, or nitrile; whereby one         or more C₁-C₂₀ carbonaceous groups can form a cyclic system.

The object of the present invention is a process to manufacture high, very high, and ultra high molecular weight polymers using the compounds of Formula I:

whereby:

-   -   M¹ is a transition metal of the 4^(th) to 6^(th) group of the         periodic table, whose oxidation level does not equal zero, and         is preferably Ti, Zr, Hf, V, Mo, Cr and Nb;     -   R¹ is hydrogen or a C₁-C₂₀-carbonaceous group or a halogen atom;     -   R² is hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom;     -   R³ and R¹⁰ are each identical or different and are each a C₁-C₂₀         carbonaceous group;     -   R⁴, R⁵, R⁶, R⁷, R⁸, R¹, R¹², R¹³, R¹⁴, and R¹⁵ are each         identical or different and are each hydrogen or a halogen atom         or a C₁-C₂₀ carbonaceous group, whereby, optionally, two or more         consecutively form a cyclic system, and preferably at least one         includes a cyclic group; and     -   R⁹ forms a bridge between the ligands, which can be shown by the         following formulas:

whereby:

-   -   M² is either silicon, germanium or tin; and     -   R¹⁶ and R¹⁷ are each identical or different and equal to         hydrogen or     -   a C₁-C₂₀ carbonaceous group or a halogen atom.

In a preferred embodiment of the invention, for Formula I:

-   -   M¹ shall be a transition metal of the 4^(th) group of the         periodic table, whose oxidation level does not equal zero, and         is preferably Ti, Zr or Hf;     -   R¹ shall be hydrogen, a C₁-C₂₀-carbonaceous group, or a halogen         atom;     -   R² shall be hydrogen, a C₁-C₂₀ carbonaceous group, or a halogen         atom;     -   R³ shall be a C₁-C₂₀ carbonaceous group, preferably one cyclized         in an α- or β-position or one in an α- or β-position branched         carbonaceous group;     -   R¹⁰ shall be a C₁-C₁₀ carbonaceous group;     -   R⁴, R⁶, R⁷, R⁸, R¹¹, R¹³, R¹⁴, and R¹⁵ shall each be equal to         hydrogen;     -   R⁵ and R¹² shall each be identical or different and shall be a         C₁-C₂₀ carbonaceous group, where, preferably one or both contain         a cyclic group such as those enumerated above; and     -   R⁹ shall form a bridge between the ligands, which can be shown         by the following formulas:

whereby:

-   -   M² is silicon; and     -   R¹⁶ and R¹⁷ are each identical or different and are each         hydrogen or     -   a C₁-C₂₀ carbonaceous group or a halogen atom.

In another embodiment of the invention, for Formula I:

-   -   M¹ shall be zirconium;     -   R¹ and R² shall be equal and stand for chlorine, methyl or         phenolate;     -   R³ shall be an isopropyl-, isobutyl-, cyclopentyl-, cyclohexyl-,         tert-butyl-, or a phenyl group;     -   R¹⁰ shall be a C₁-C₁₀ carbonaceous alkyl group, preferably a         C₁-C₆ carbonaceous alkyl group; and     -   R⁴, R⁶, R⁷, R⁸, R¹¹, R¹³, R¹⁴, and R¹⁵ shall each be hydrogen;     -   R⁵ and R¹² shall be identical and include a phenyl group which         supports a C₁-C₄ alkyl group, preferably in the para-position;         and     -   R⁹ shall form a bridge between the ligands, which can be shown         by the following formulas:

whereby:

-   -   M² is silicon; and     -   R¹⁶ and R¹⁷ are each identical or different and are hydrogen or         a C₁-C₂₀ carbonaceous group or a halogen atom.

In a more preferred embodiment of the invention, Formula I represents a bridged metallocene catalyst, whereby:

-   -   M¹ is zirconium;     -   R¹ and R² are identical and each is chlorine;     -   R³ and R¹⁰ are identical or different and are selected from a         methyl, ethyl, or isopropyl group;     -   R⁴, R⁶, R⁷, R⁸, R¹¹, R¹³, R¹⁴, and R¹⁵ are each a hydrogen;     -   R⁵ and R¹² are identical and are selected from a hydrogen or a         p-t-butylphenyl group; and     -   R⁹ shall form a bridge between the ligands, which can be shown         by the following formula:

whereby:

-   -   M² is silicon; and     -   R¹⁶ and R¹⁷ are each identical and are a methyl group.

Illustrative but non-limiting examples for compounds of Formula I are:

-   -   Dimethylsilandiyl-bis(2-methyl-indenyl)zirconium dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-isopropyl-phenyl)indenyl)(2-methyl-4-(p-isopropyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-tert.-butyl-phenyl)indenyl)(2-methyl-4-(p-tert.-butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-tert.-butyl-phenyl)indenyl)(2,7-dimethyl-4-(p-tert.-butyl-phenyl)         indenyl)-zirconium dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-tert.-butyl-phenyl)indenyl)(2,5,6,7-tetramethyl-4-(p-tert.-butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-6-methyl-4-(p-tert.-butyl-phenyl)indenyl)(2,6-dimethyl-4-(p-tert.-butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-sec.-butyl-phenyl)indenyl)(2-methyl-4-(p-sec.butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-cyclohexyl-phenyl)indenyl)(2-methyl-4-(p-cyclohexyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-trimethylsilyl-phenyl)indenyl)(2-methyl-4-(p-trimethylsilyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-adamantyl-phenyl)indenyl)(2-methyl-4-(p-adamantyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-tris(trifluoromethyl)methyl-phenyl)indenyl)(2-methyl-4-(p-tris(trifluoromethyl)methyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-phenyl-indenyl)(2-methyl-4-(p-tert.-butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-tert.-butyl-phenyl)indenyl)(2-methyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-tert-butyl-phenyl)indenyl)(2,7-dimethyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-tert.-butyl-phenyl)indenyl)         (2,5,6,7-tetramethyl-4-phenyl-indenyl)-zirconium dichloride,     -   Dimethylsilandiyl-(2-isopropyl-6-methyl-4-(p-tert.-butyl-phenyl)indenyl)(2,6-dimethyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-phenyl-indenyl)(2,7-dimethyl-4-(p-tert.-butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-phenyl-indenyl)(2,5,6,7-tetramethyl-4-(p-tert.-butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-6-methyl-4-phenyl-indenyl)(2,6-dimethyl-4-(p-tert.-butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(p-tert.-butyl-phenyl)indenyl)(2-methyl-4-(4-naphthyl)-indenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-isopropyl-4-(4-naphthyl)-indenyl)indenyl)(2-methyl-4-(p-tert.-butyl-phenyl)indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-[4,5]-benzo-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-indenyl)zirconium dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(1-naphthyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(2-naphthyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-phenyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-tert.-butyl-indenyl)zirconium         dichloride,         Dimethylsilandiyl-bis(2-isopropyl-4-isopropyl-indenyl)zirconium         dichloride,         Dimethylsilandiyl-bis(2-isopropyl-4-ethyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-acenaphth-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2,4-diisopropyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-methyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2,4,6-triisopropyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2,4,5-triisopropyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-5-isobutyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-5-t-butyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-tert-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-ethyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-trifluoromethyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-methoxy-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-tert-butyl-phenyl)-indenyl)zirconium         dimethyl,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dimethyl,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-ethyl-phenyl)-indenyl)zirconium         dimethyl,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-trifluoromethyl-phenyl)indenyl)zirconium         dimethyl,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-methoxy-phenyl)-indenyl)zirconium         dimethyl,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-tert.-butyl-phenyl)-indenyl)hafnium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-tert.-butyl-phenyl)-indenyl)titanium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-n-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-n-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-sec-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-ethyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-n-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-n-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-pentyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-cyclohexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-sec-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-phenyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-(4′-ethyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-(4′-iso-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-(4′-n-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-(4′-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-(4′-cyclohexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-(4′-sec-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-propyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-phenyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-ethyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-n-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-iso-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-n-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-cyclohexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-sec-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-n-butyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-phenyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-ethyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-n-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-iso-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-n-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-n-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-cyclohexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-sec-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-hexyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-phenyl-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-ethyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-n-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-iso-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-n-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-n-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-cyclohexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-sec-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-phenyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconiumbis(dimethylamine),     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconium         dibenzyl,     -   Dimethylsilandiyl-bis(2-ethyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-(4′-tert.-butyl-phenyl)-indenyl)zirconium         dimethyl,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-5-azapentalene)(2-isopropyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-azapentalene)(2-isopropyl-4-(4′-methyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-(4′-ethyl-phenyl)indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropyl-4-(4′-n-propyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-(4′-isopropyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-azapentalene)(2-isopropyl-4-(4′-isopropyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2,5-dimethyl-6-thiapentalene)(2-isopropyl-4-(4′-isopropyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-oxapentalene)(2-isopropyl-4-(4′-isopropyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-azapentalene)(2-isopropyl-4-(4′-n-butyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-5-thiapentalene)(2-isopropyl-4-(4′-n-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-oxapentalene)(2-isopropyl-4-(4′-n-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropyl-4-(4′-s-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-oxapentalene)(2-isopropyl-4-(4′-s-butyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-(4′-tert.-butyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-azapentalene)(2-isopropyl-4-(4′-tert.-butyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-(4′-n-pentyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-N-phenyl-6-azapentalene)(2-isopropyl-4-(4′-n-pentyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-oxapentalene)(2-isopropyl-4-(4′-n-pentyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-(4′-n-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropyl-4-(4′-n-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-thiapentalene)(2-isopropyl-4-(4′-n-hexyl-phenyl)-indenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2,5-Dimethyl-4-thiapentalene)(2-isopropyl-4-(4′-n-hexyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2,5-Dimethyl-6-thiapentalene)(2-isopropyl-4-(4′-n-hexyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2,5-dimethyl-6-thiapentalene)(2-isopropyl-4-(4′-cyclohexyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-(4′-trimethylsilyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropyl-4-(4′-trimethylsilyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-5-thiapentalene)(2-isopropyl-4-(4′-trimethylsilyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-thiapentalene)(2-isopropyl-4-(4′-trimethylsilyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2,5-Dimethyl-4-azapentalene)(2-isopropyl-4-(4′-adamantyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropyl-4-(4′-adamantyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-thiapentalene)(2-isopropyl-4-(4′-adamantyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2,5-dimethyl-4-thiapentalene)(2-isopropyl-4-(4′-adamantyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-(4′-tris(trifluoromethyl)-methyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2,5-Dimethyl-4-azapentalene)(2-isopropyl-4-(4′-tris(trifluoromethyl)methyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropyl-4-(4′-tris(trifluoromethyl)methyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-thiapentalene)(2-isopropyl-4-(4′-tris(trifluoromethyl)-methyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-N-phenyl-6-azapentalene)(2-isopropyl-4-(4′-tert-butyl-phenyl)-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropylindenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-N-phenyl-4-azapentalene)(2-isopropylindenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropylindenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-5-thiapentalene)(2-isopropylindenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-thiapentalene)(2-isopropylindenyl)zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-5-azapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-azapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-N-phenyl-4-azapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-N-phenyl-5-azapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-5-thiapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-thiapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-oxapentalene)(2-isopropyl-4-phenyl-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-azapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-N-phenyl-4-azapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-N-phenyl-5-azapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-N-phenyl-6-azapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-thiapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-5-thiapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-thiapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-4-oxapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-5-oxapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-(2-methyl-6-oxapentalene)(2-isopropyl-4,5-benzo-indenyl)-zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-azapentalene)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-N-phenyl-4-azapentalene)zirconium         dichloride,     -   Dimethylsilandiyl-bis(2-isopropyl-4-thiapentalene)zirconium         dichloride,         as well as the corresponding titanium and hafnium compounds and         also various bridges of dimethylsilandiyl according to Formula I         such as dimethylmethandiyl, diphenylmethandiyl, ethandiyl,         1,2-dimethylethandiyl, dipropylsilandiyl, dibutylsilandiyl,         dipentylsilandiyl, dihexylsilandiyl, diheptylsilandiyl,         dioctylsilandiyl, dinonylsilandiyl, didecylsilanediyl,         diundecylsilandiyl, didodecylsilandiyl.

The synthesis of the compounds of Formula I according to the invention can be conducted according to processes known to one skilled in the art. An example therefor is set forth in the following schematic.

The compounds of Formula I according to the invention are particularly suited to be components of catalyst systems to manufacture polyolefins through the polymerization of at least one olefin in the presence of a catalyst that contains at least one compound of Formula I according to the invention, and optionally at least one co-catalyst.

Ethylene is preferred as the olefin. In a preferred embodiment of the invention, ethylene is polymerized using the catalysts of the invention, whereby polymerization is understood to be both the homo-polymerization of ethylenes as well as the co-polymerization of ethylene with other olefins. The ethylene used in the process can, if desired, contain still other olefins that are selected from the group that is formed by: 1-olefins (or alpha-olefins) with 3-20, preferably 3 to 10 C atoms, such as propene, 1-butene, 1-pentene, 1-hexene, 1-octene, 1-decene, or 4-methyl-1-pentene; dienes such as 1,3-butadiene or 1,4-hexadiene; and cyclo-olefins such as styrene, norbornene, methyl norbornene, vinyl norbornene, cyclopentadiene, norbornadiene, ethyl norbornadiene or tetracyclododecene; as well as mixtures of same.

Particular preference is given to co-polymerizing the ethylene used with one or more olefins with 3 to 8 C atoms such as propene, 1-butene, 1-pentene, 1-hexene, styrene or butadiene.

A co-monomer fraction of 0.1 to 10% is suitable, preferably 0.5 to 9% and in particular 2 to 5%. Particular preference is given to the co-polymerization of ethylene with the co-monomer propene.

Further preference is given to the process according to the invention whereby the ethylene used is homo-polymerized, or co-polymerized with propene.

Particular preference is given to the process according to the invention whereby the ethylene used is homo-polymerized.

The ethylene polymers and co-polymers manufactured with the process according to the invention are high to ultra high molecular weight, since they have a viscosimetrically determined molecular weight of at least about 0.7×10⁶ g/mol and preferably greater than 1×10⁶ g/mol. Preference is given to polyethylenes with a molecular weight of greater than 1×10⁶ g/mol that can be obtained using the process according to the invention.

The viscosimetric measurements are made in DECALIN® at 135° C. and a concentration of 0.1 g (polymer)/1 L (DECALIN®). The molecular weight can be derived from the viscosity number.

The polymerization is conducted at a temperature of −20 to 300° C., preferably 0 to 200° C., most especially preferred at 20 to 100° C. The pressure is from 0.5 to 2000 bar, preferably 1 to 64 bar. The polymerization can be conducted in solution, in bulk, in suspension or in emulsion, continuously or in batches, in one or more stages. Suitable solvents for the polymerization are, for example, aliphatic hydrocarbons such as pentane, hexane and the like or aromatic hydrocarbons such as benzene, toluene, xylene and the like, or ethers such as diethyl ether, dibutyl ether, methyl-tert-butyl ether, tetrahydrofuran, dioxane, anisole, diphenyl ether and ethyl-phenyl ether, as well as halogenated solvents such as dichloromethane, trichloromethane, chloro-benzene, bromo-benzene and the like. Mixtures of various solvents in various proportions can also be used according to the invention.

Ultra high molecular weight ethylene polymers and co-polymers are obtained through the polymerization of at least one olefin in the presence of catalyst systems of at least one compound of Formula I and one co-catalyst.

In a preferred embodiment of the invention, the catalyst system used in the process according to the invention contains at least one co-catalyst.

The co-catalyst that, together with at least one transition metal compound of Formula I, forms the catalyst system, contains at least one aluminoxane compound, or another Lewis acid, or an ionic compound, which reacts with the transition metal compound to convert it into a cationic compound.

Particular preference is given to catalyst systems that contain at least one Lewis acid as co-catalyst.

As aluminoxane, preference is given to using a compound of the general Formula II. (R AlO)q  Formula II Other suitable aluminoxanes may be cyclic, and can have the structure shown, for example, in Formula III

or may be linear as in Formula IV

or may be of a cluster type as in Formula V.

Such aluminoxanes are, for example, described in JACS 117 (1995), 6465-74, Organometallics 13 (1994), 2957-2969.

The radical R in the Formulas II, III, IV and V may be identical or different and are each a C₁-C₂₀-hydrocarbon group such as a C₁-C₆ alkyl group, a C₆-C₁₈ aryl group, benzyl or hydrogen, and q stands for an integer of 2 to 50, preferably 10 to 35. Preferably, the radicals R are identical and are each methyl, isobutyl, n-butyl, phenyl or benzyl, in particular methyl.

If the radicals R are different, they are preferably methyl and hydrogen, methyl and isobutyl, or methyl and n-butyl, containing hydrogen or isobutyl or n-butyl preferably up to 0.01-40% (number of radicals R).

The aluminoxane can be manufactured in various ways according to known processes. One of the methods is, for example, reacting an aluminum hydrocarbon compound and/or a hydridoaluminum hydrocarbon compound with water (gaseous, solid, liquid or bound—for example as water of crystallization) in an inert solvent (such as toluene).

To prepare an aluminoxane having different alkyl groups R, two different aluminum trialkyls (AIR₃+AIR′₃), corresponding to the desired composition and reactivity, are reacted with water (see S. Pasynkiewicz, Polyhedron 9 (1990) 429 and EP-A-0,302,424).

Regardless of the type of preparation, a variable content of unreacted aluminum feed compound, present in free form or as an adduct, is common to all aluminoxane solutions.

As Lewis acid, preference is given to using at least one boron or organoaluminum compound containing C₁-C₂₀ carbonaceous groups, including branched or unbranched alkyl or haloalkyl groups, such as methyl, propyl, isopropyl, isobutyl, trifluoromethyl, and unsaturated groups including aryls or haloaryls, such as phenyl, tolyl, benzene groups, p-fluorophenyl, 3,5-difluorophenyl, pentachlorophenyl, pentafluorophenyl, 3,4,5 trifluorophenyl and 3,5 di(trifluoromethyl)phenyl.

Examples of Lewis acids are trimethylaluminum, triethylaluminum, triisobutylaluminum, tributylaluminum, trifluoroborane, triphenylborane, tris(4-fluorophenyl)borane, tris(3,5-difluorophenyl)borane, tris(4-fluoromethylphenyl)borane, tris(pentafluorophenyl)borane, tris(tolyl)borane, tris(3,5-dimethylphenyl)borane, tris(3,5-difluorophenyl)borane, and/or tris(3,4,5-trifluorophenyl)borane. Particular preference is given to tris(pentafluorophenyl)borane.

As ionic cocatalysts, preference is given to using compounds that contain a noncoordinating anion, such as tetrakis(pentafluorophenyl)-borate, tetraphenylborate, SbF₆—, CF₃SO₃— or ClO₄—.

As cationic counterions, use is made of protonated Lewis bases such as, for example, methyl amine, aniline, N,N-dimethylbenzylamine, as well as their derivatives, N,N-dimethylcyclohexylamine and its derivatives, dimethylamine, diethylamine, N-methylaniline, diphenylamine, N,N-dimethylaniline, trimethylamine, triethylamine, tri-n-butylamine, methyldiphenylamine, pyridine, p-bromo-N,N-dimethylaniline, p-nitro-N,N-dimethylaniline, triethylphosphine, triphenylphosphine, diphenylphosphine, tetrahydrothiophene, or triphenylcarbenium.

Examples of such ionic compounds are:

-   -   Triethylammoniumtetra(phenyl)borate,     -   Tributylammoniumtetra(phenyl)borate,     -   Trimethylammoniumtetra(tolyl)borate,     -   Tributylammoniumtetra(tolyl)borate,     -   Tributylammoniumtetra(pentafluorophenyl)borate,     -   Tributylammoniumtetra(pentafluorophenyl)aluminate,     -   Tripropylammoniumtetra(dimethylphenyl)borate,     -   Tributylammoniumtetra(trifluoromethylphenyl)borate,     -   Tributylammoniumtetra(4-fluorophenyl)borate,     -   N,N-Dimethylaniliniumtetra(phenyl)borate,     -   N,N-Diethylaniliniumtetra(phenyl)borate,     -   N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)borate,     -   N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)aluminate,     -   Di(propyl)ammoniumtetrakis(pentafluorophenyl)borate,     -   Di(cyclohexyl)ammoniumtetrakis(pentafluorophenyl)borate,     -   Triphenylphosphoniumtetrakis(phenyl)borate,     -   Triethylphosphoniumtetrakis(phenyl)borate,     -   N,N-Dimethylcyclohexylammoniumtetrakis(pentafluorophenyl)borate,     -   N,N-Dimethylbenzylammoniumtetrakis(pentafluorophenyl)borate,     -   Diphenylphosphoniumtetrakis(phenyl)borate,     -   Tri(methylphenyl)phosphoniumtetrakis(phenyl)borate,     -   Tri(dimethylphenyl)phosphoniumtetrakis(phenyl)borate,     -   Triphenylcarbeniumtetrakis(pentafluorophenyl)borate,     -   Triphenylcarbeniumtetrakis(pentafluorophenyl)aluminate,     -   Triphenylcarbeniumtetrakis(phenyl)aluminate,     -   Ferroceniumtetrakis(pentafluorophenyl)borate and/or     -   Ferroceniumtetrakis(pentafluorophenyl)aluminate.

Preference is given to triphenylcarbeniumtetrakis(pentafluorophenyl)borate and/or N,N-dimethylaniliniumtetrakis(pentafluorophenyl)borate.

Mixtures of at least one Lewis acid and at least one ionic compound can also be used.

Further suitable cocatalyst components are borane or carborane compounds such as:

-   -   7,8-dicarbaundecaborane(13),     -   Undecahydride-7,8-dimethyl-7,8-dicarbaundecaborane,     -   Dodecahydride-1-phenyl-1,3-di-carbanonaborane,     -   Tri(butyl)ammoniumundecahydride-8-ethyl-7,9-dicarbaundecaborate,     -   4-carbanonaborane(14)bis(tri(butyl)ammonium)nonaborate,     -   Bis(tri(butyl)ammonium)undecaborate,     -   Bis(tri(butyl)ammonium)dodecaborate,     -   Bis(tri(butyl)ammonium)decachlorodecaborate,     -   Tri(butyl)ammonium-1-carbadecaborate,     -   Tri(butyl)ammonium-1-carbadodecaborate,     -   Tri(butyl)ammonium-1-trimethylsilyl-1-carbadecaborate,     -   Tri(butyl)ammoniumbis(nonahydride-1,3-di-carbonnonaborate)cobaltate(III),         and     -   Tri(butyl)ammoniumbis(undecahydride-7,8-carbaundecaborate)ferrate(III).

Further useful co-catalyst systems are combinations of at least one of the aforementioned amines and if desired, a support with organo-element compounds, as they are described in WIPO Publication No. WO 99/40129 (and equivalent U.S. Pat. No. 6,482,902), the entireties of which are incorporated herein by reference.

The supports with organoelement compounds named in WO99/40129 are also components of this invention.

Preferred components of these co-catalyst systems are the compounds of Formulas A and B,

whereby:

-   -   R¹⁸ is a hydrogen atom, a halogen atom, a C₁-C₂₀ carbonaceous         group, in particular C₁-C₂₀ alkyl, C₁-C₂₀ haloalkyl, C₁-C₁₀         alkoxy, C₆-C₂₀ aryl, C₆-C₂₀ haloaryl, C₆-C₂₀ aryloxy, C₇-C₂₀         arylalkyl, C₇-C₄₀ haloarylalkyl, C₇-C₂₀ alkylaryl or C₇-C₂₀         haloalkylaryl. R¹⁸ can also be an OSiR₃ group, whereby R is         identical or different and has the same meaning as the         definition of R¹⁸ provided immediately above.

Further preferred co-catalysts are general compounds that are formed by the reaction of at least one compound of Formula C and/or D and/or E with at least one compound of formula F.

whereby:

-   -   R¹⁸ has the same meaning as mentioned above; and     -   R¹⁹ can be a hydrogen atom or a boron free C₁-C₂₀ carbonaceous         group such as C₁-C₂₀ alkyl, C₆-C₂₀ aryl, C₇-C₂₀ arylalkyl,         C₇-C₂₀ alkylaryl; and     -   X¹ is an element of the 16^(th) group of the periodic table or         an NR group, whereby R is a hydrogen atom or a C₁-C₂₀         hydrocarbon radical such as C₁-C₂₀-Alkyl or C₁-C₂₀ Aryl; and     -   L is an element of the 16^(th) group of the periodic table or an         NR group, whereby R is a hydrogen atom or a C₁-C₂₀ hydrocarbon         radical such as C₁-C₂₀-alkyl or C₁-C₂₀ aryl;     -   f is an integer from 0 to 3; and     -   g is an integer from 0 to 3.

If desired, the organoelement compounds are combined with an organometallic compound of Formulas II to V and/or VI, [M³R²⁰ _(r)]_(k)  Formula VI whereby:

-   -   M³ is an element of the 1^(st), 2^(nd), or 13^(th) group of the         periodic table; R²⁰ is identical or different and is a hydrogen         atom, a halogen atom, a C₁-C₄₀ carbonaceous group, in particular         a C₁-C₂₀ alkyl, a C₆-C₂₀ aryl, a C₇-C₂₀ aryl-alkyl, or a C₇-C₂₀         alkyl-aryl group; r is an integer from 1 to 3; and k is an         integer of 1 to 4.

Examples for the co-catalytically effective compounds of Formulas A and B are:

The organometallic compounds of Formula F are preferably uncharged Lewis acids. Examples of preferred organometallic compounds of Formula F are trimethylaluminum, triethylaluminum, triisopropylaluminum, trihexylaluminum, trioctylaluminum, tri-n-butylaluminum, tri-n-propylaluminum, triisoprenealuminum, dimethylaluminum monochloride, diethylaluminum monochloride, diisobutylaluminum monochloride, methylaluminum sesquichloride, ethylaluminum sesquichloride, dimethylaluminum hydride, diethylaluminum hydride, diisopropylaluminum hydride, dimethylaluminum-(trimethylsiloxide), dimethylaluminum(triethylsiloxide), phenylalane, pentafluorophenylalane, and o-tolylalane.

Further co-catalysts, which may be in unsupported or supported form, are the compounds mentioned in EP-A-924223 (equivalent of U.S. Pat. No. 6,444,603), EP-A-601830 (equivalent of U.S. Pat. No. 5,449,650), EP-A-824112 (equivalent of U.S. Pat. No. 6,329,313), EP-A-824113 (equivalent of U.S. Pat. No. 6,124,231), EP-A-811627 (equivalent of DE-A-19622207 and U.S. Pat. No. 6,255,531), WO 97/11775 (equivalent of U.S. Pat. No. 6,271,164), and DE-A-19606167 (equivalent of U.S. Pat. No. 6,350,829), the entireties of which are incorporated herein by reference.

Moreover, the catalysts according to the invention can be homogeneously as well as heterogeneously supported.

In a preferred embodiment, the compound of Formula I used in the process according to the invention is used in a supported form.

The support component of the catalyst system can be any organic or inorganic inert solid, in particular a porous support such as talc, inorganic oxides and finely divided polymer powder (e.g., polyolefin).

Suitable inorganic oxides may be found in the groups 2, 3, 4, 5, 13, 14,15, and 16 of the periodic table. Examples for the oxides preferred as supports include silicon dioxide, aluminum oxide, and also mixed oxides of the elements calcium, aluminum, silicon, magnesium, titanium and corresponding oxide mixtures as well as hydrotalcite. Other inorganic oxides that can be used either alone or in combination with the aforementioned preferred oxidic supports, are, e.g., MgO, ZrO₂, TiO₂ or B₂O₃, to name a few.

The support materials used have a specific surface area in the range from 10 to 1000 m²/g, a pore volume in the range from 0.1 to 5 ml/g and a mean particle size of 1 to 500 μm. Preference is given to supports with a specific surface area in the range of 50 to 500 m²/g, a pore volume in the range from 0.5 to 3.5 ml/g and a mean particle size in the range of 5 to 350 μm. Particular preference is given to supports having a specific surface area in the range from 200 to 400 m²/g, a pore volume in the range from 0.8 to 3.0 ml/g, and a mean particle size of 10 to 200 μm.

If the support material naturally exhibits a low moisture content or residual solvent content, the dehydration or drying before use can be omitted. If this is not the case, as when using silica gel as support material, dehydration or drying is advisable. Thermal dehydration or drying of the support material can be carried out under a vacuum and a simultaneous blanketing with inert gas (e.g., nitrogen). The drying temperature is in the range from 100 to 1000° C., preferably from 200 to 800° C. The pressure is not critical in this instance. The drying process can last from 1 to 24 hours. Shorter or longer drying times are possible, provided that establishment of equilibrium with the hydroxyl groups on the support surface can take place under the conditions chosen, which normally takes from 4 to 8 hours.

Dehydration or drying of the support material can also be carried out by chemical means, by reacting the adsorbed water and the hydroxyl groups on the surface with suitable passivating agents. Reaction with the passivating reagent can convert all or part of the hydroxyl groups into a form which does not lead to any adverse interaction with the catalytically active centers. Suitable passivating agents are, for example, silicon halides and silanes, e.g. silicon tetrachloride, chlortrimethylsilane, dimethylamino trichlorosilane, or organometallic compounds of aluminum, boron and magnesium, for example trimethylaluminum, triethylaluminum, triisobutylaluminum, triethylborane, or dibutylmagnesium. Chemical dehydration or passivation of the support material is carried out, for example, by reacting a suspension of the support material in a suitable solvent with the passivating reagent either in pure form or as a solution in a suitable solvent in the absence of air and moisture. Suitable solvents are, for example, aliphatic or aromatic hydrocarbons such as pentane, hexane, heptane, toluene or xylene. Passivation is carried out at from 25° C. to 120° C., preferably from 50° C. to 70° C. Higher and lower temperatures are possible. The reaction time is from 30 minutes to 20 hours, preferably from 1 to 5 hours. After the chemical dehydration is complete, the support material is isolated by filtration under inert conditions, washed one or more times with suitable inert solvents as described above and subsequently dried in a stream of inert gas or under reduced pressure.

Organic support materials such as finely divided polyolefin powders (e.g., polyethylene, polypropylene or polystyrene) can also be used and should likewise be freed of adhering moisture, solvent radicals or other impurities by appropriate purification and drying operations prior to use.

To prepare the supported catalyst system, at least one of the above-described compounds of Formula I is brought in contact with at least one co-catalyst component in a suitable solvent, preferably giving a soluble reaction product, an adduct or a mixture.

The preparation so obtained is then mixed with the dehydrated or passivated support material, the solvent removed and the resulting supported catalyst system dried, to ensure that all or most of the solvent is removed from the pores of the support materials. The supported catalyst is obtained as a free flowing powder.

Another object of the present invention is a process to provide a free flowing and, if desired, pre-polymerized supported catalyst system comprising the following steps:

-   -   a) preparation of a mixture of at least one compound of Formula         I and at least one co-catalyst in a suitable solvent or         suspension medium;     -   b) application of the mixture obtained from Step a) to a porous,         preferably inorganic, dehydrated support;     -   c) removal of most of the solvent from the resulting mixture;     -   d) isolation of the supported catalyst system; and     -   e) if desired, a pre-polymerization of the supported catalyst         system obtained using one or several olefinic monomer(s), to         obtain a pre-polymerized supported catalyst system.

Preferred solvents in step a) are hydrocarbons and hydrocarbon mixtures that are liquid at the reaction temperature chosen and in which the individual components are preferably dissolved. The solubility of the individual components is, however, not a prerequisite, as long as the reaction product from the compound of Formula I and the co-catalyst is soluble in the solvent chosen. Examples for the suitable solvents include alkanes such as pentane, isopentane, hexane, heptane, octane, and nonane; cycloalkanes such as cyclopentane and cyclohexane; and aromatics such as benzene, toluene, ethylbenzene and diethylbenzene. Very particular preference is given to toluene.

The amounts of aluminoxane and compound of Formula I used in the preparation of the supported catalyst system can be varied over a wide range. Preference is given to a molar ratio of aluminum to transition metal in the compound of Formula I of 10:1 to 1000:1, very particularly preferably from 50:1 to 500:1.

In the case of methylaluminoxane preference is given to using 30% strength toluene solutions; the use of 10% strength solutions is, however, also possible. To carry out the preactivation, the compound of Formula I in the form of a solid is dissolved in a solution of the aluminoxane in a suitable solvent. It is also possible to dissolve the compound of Formula I separately in a suitable solvent and then to combine this solution with the aluminoxane solution. Preference is given to using toluene.

The preactivation time is from 1 minute to 200 hours.

The preactivation can take place at room temperature (25° C.). The use of higher temperatures can, in certain cases, shorten the time required for the preactivation and produce an additional increase in activity. In this case, a higher temperature means a range from 50° C. to 10° C.

The pre-activated solution or the mixture is then combined with an inert support material, usually silica gel, which is in the form of a dry powder or as a suspension in one of the aforementioned solvents.

Preference is given to using the support material in the form of powder. The order of addition is immaterial. The preactivated metallocene co-catalyst solution or the metallocene co-catalyst mixture can be added to the support material or else the support material can be introduced to the catalyst mixture.

The volume of the preactivated solution or the metallocene co-catalyst mixture can exceed 100% of the total pore volume of the support material used or else can be up to 100% of the total pore volume.

The temperature at which the preactivated solution or the metallocene co-catalyst mixture is brought in contact with the support material can vary in the range from 0° C. to 100° C. Lower or higher temperatures are, however, also possible.

All or the major part of the solvent is subsequently removed from the supported catalyst system, whereby the mixture can be stirred and, if necessary, also heated. Preference is given to removing both the visible portion of the solvent as well as the portion in the pores of the support material. The removal of the solvent can be carried out in a conventional fashion with application of vacuum and/or flushing with inert gas. In the drying process, the mixture can be heated until the free solvent has been removed, which usually takes from 1 to 3 hours at a preferred temperature of from 30° C. to 60° C. The free solvent is the visible portion of solvent in the mixture. In this context, residual solvent is the portion which is enclosed in the pores. As an alternative to complete removal of the solvent, it is also possible for the supported catalyst system to be dried only to a particular residual solvent content, with the free solvent having been completely removed. The supported catalyst system can subsequently be washed with a low-boiling hydrocarbon such as pentane or hexane and dried again.

The supported catalyst system can either be used directly for the polymerization of olefins or can be prepolymerized using one or more olefinic monomers prior to use in a polymerization process. An example of the prepolymerization of supported catalyst systems is described in WO 94/28034.

A small amount of an olefin, preferably an α-olefin (for example vinyl cyclohexane, styrene or phenyldimethylvinylsilane) as modifying component or an anti-static (as described in U.S. patent application Ser. No. 08/365,280) can be added as additive during or after the preparation of the supported catalyst system. The molar ratio of additive to metallocene components (compound according to Formula I) is preferably from 1:1000 to 1000:1, very particularly preferably from 1:20 to 20:1.

Another object of the invention is the use of the catalyst systems according to the invention, containing at least one compound according to Formula I and at least one co-catalyst to manufacture high to ultra high molecular weight ethylene homo- or co-polymers.

Particular preference is given to the catalyst system being present in a supported form.

The invention is depicted through the following examples, which are not intended to limit the invention, the scope of which is set forth in the appended claims.

EXAMPLES

General information: preparation and handling of organometallic compounds were carried out in the absence of air and moisture under argon (using the Schlenk technique or a glove box). All solvents required were purged with argon and dried over molecular sieves before use.

The following catalysts are used in the examples:

Example 1 Production of the Supported Catalysts

1. Activation:

In an annealed flask under inert gas 0.128 mmol catalyst is dissolved in 20 ml toluene and mixed with 6 ml (28.8 mmol, 1.672 g) methylaluminoxane (MAO; 30% in toluene). The mixture is stirred for one hour at room temperature.

2. Support:

In an annealed flask under inert gas 6 g SiO₂ (Grace XPO 2107, dried) is placed and suspended with 30 ml abs. toluene. A suspension results that can be slightly stirred, to which the activated catalyst (from 1) is then added. It is stirred for 10 min and then the solvent is removed in a vacuum to up to no more than 5% residual moisture.

Examples 2-6 Homopolymerization of Ethylene

In a 2 L steel autoclave 1.5 L EXXSOL® is placed and mixed with 15 mmol of an aluminum alkyl (e.g., tri-isobutylaluminum). The reactor is then brought to the desired temperature and an ethylene pressure of 7-15 bar is built up. At the start of the polymerization 9 μmol of the relevant catalyst (see Table 1) suspended in EXXSOL® is added. It is polymerized for one hour and the reaction is stopped when the ethylene pressure degrades. The polymer is filtered and dried in a vacuum at 80° C. Finally, the yield and the molecular weight are determined.

TABLE 1 Pressure Example Catalyst C2 Temperature Yield M_(v) 2 1 10 bar 70° C. 70 g 0.7 × 10⁶ g/mol 3 2 10 bar 70° C. 61 g 2.2 × 10⁶ g/mol 4 3 10 bar 70° C. 64 g 1.1 × 10⁶ g/mol 5 4 10 bar 70° C. 98 g 1.8 × 10⁶ g/mol 6 5 10 bar 70° C. 114 g  2.7 × 10⁶ g/mol

The above table therefore shows that heterogeneous polymerization according to the inventive process using the bridged metallocene catalysts of the invention achieves high to ultra high molecular weight polyethylene products. Note that ultra high molecular weight products are formed only when the bridged metallocene catalysts of the invention having substituent carbonaceous groups with more than one carbon, particularly at the R³ position, are used. Additionally, in several embodiments, higher substitution of the inventive catalyst at the R³ position in combination with higher substitution at the R⁵ and R¹² positions provide for significantly improved yields.

While the invention has been illustrated in connection with several examples, modifications to these examples within the spirit and scope of the invention will be readily apparent to those of skill in the art. In view of the foregoing discussion, relevant knowledge in the art and references discussed above, the disclosures of which are all incorporated herein by reference, further description is deemed unnecessary. 

1. A process of manufacturing high, very high, and ultra high molecular weight polymers comprising predominantly ethylene monomers, wherein the process comprises reacting ethylene monomers, and optionally additional olefin monomers, in the presence of a catalyst system which includes a catalytic compound of Formula I to produce a polymer having a viscosimetrically-determined molecular weight of 0.7×10⁶ g/mol or greater

whereby: M¹ is a transition metal of the 4^(th) to 6^(th) group of the periodic table, wherein the oxidation level of said transition metal does not equal zero; R¹ is hydrogen or a C₁-C₂₀-carbonaceous group or a halogen atom; R² is hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom; R³ and R¹⁰ are each identical or different and are each a C₁-C₂₀ carbonaceous group; R⁴, R⁵, R⁶, R⁷, R⁸, R¹¹, R¹², R¹³, R¹⁴, and R¹⁵ are each identical or different and are each hydrogen or a halogen atom or a C₁-C₂₀ carbonaceous group, whereby, optionally, two or several consecutively form a cyclic system; and R⁹ is a bridge between the ligands, which is represented by one of the following formulas:

whereby: M² is either silicon, germanium or tin; and R¹⁶ and R¹⁷ are each identical or different and are each hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom; with the proviso that when R⁵ or R¹² constitutes a phenyl group supporting an alkyl group, the alkyl group is present in a para position.
 2. The process according to claim 1, wherein M¹ is selected from the group consisting of Ti, Zr, Hf, V, Mo, Cr and Nb.
 3. The process according to claim 1, wherein at least one of R⁴, R⁵, R⁶, R⁷, R⁸, R¹¹, R¹², R¹³, R¹⁴, and R¹⁵ includes a cyclic group.
 4. The process according to claim 1, wherein for the compound of Formula I: M¹ is a transition metal of the 4^(th) group of the periodic table, wherein the oxidation level of said transition metal does not equal zero; R¹ is hydrogen, a C₁-C₂₀-carbonaceous group, or a halogen atom; R² is hydrogen, a C₁-C₂₀ carbonaceous group, or a halogen atom; R³ is a C₁-C₂₀ carbonaceous group; R¹⁰ is a C₁-C₁₀ carbonaceous group; R⁴, R⁶, R⁷, R⁸, R¹¹, R¹³, R¹⁴ and R¹⁵ are each hydrogen; R⁵ and R¹² are each identical or different and are a C₁-C₂₀ carbonaceous group, of which at least one includes a cyclic group; and R⁹ is a bridge between the ligands, which is represented by one of the following formulas:

whereby: M² is silicon; and R¹⁶ and R¹⁷ are each identical or different and are each hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom.
 5. The process according to claim 4, wherein R⁵ and R¹² are identical or different and are selected from the group consisting of C₆-C₂₀ aryl, C₆-C₂₀ fluoroaryl, C₆-C₂₀ aryloxy, C₇-C₂₀ arylalkyl, C₇-C₂₀ alkylaryl, C₇-C₂₀ aryloxyalkyl, C₁₂-C₂₀ aryloxyaryl, C₅-C₂₀ heteroaryl, C₄-C₂₀ heterocycloalkyl, C₈-C₂₀ arylalkenyl, and C₈-C₂₀ arylalkinyl.
 6. The process according to claim 4, wherein both of R⁵ and R¹² include a cyclic group.
 7. The process according to claim 4, wherein R³ is an α- or β-position branched carbonaceous group or a carbonaceous group cyclized in a α- or β-position.
 8. The process according to claim 1, wherein for the compound of Formula I: M¹ is zirconium; R¹ and R² are identical and are each chlorine, methyl or phenolate; R³ is an isopropyl-, isobutyl-, cyclopentyl-, cyclohexyl-, tert-butyl-, or a phenyl group; R¹⁰ is a C₁-C₁₀ carbonaceous group and is an alkyl group; R⁴, R⁶, R⁷, R⁸, R¹¹, R¹³, R¹⁴, and R¹⁵ are each hydrogen; R⁵ and R¹² are identical or different and are each a C₁-C₂₀ carbonaceous group, wherein at least one includes a phenyl group which supports a C₁-C₄ alkyl group; and R⁹ is a bridge between the ligands, which is represented by one of the following formulas:

whereby: M² is silicon; and R¹⁶ and R¹⁷ are each identical or different and are hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom.
 9. The process according to claim 8, wherein R⁵ and R¹² are identical and include a phenyl group which supports a C₁-C₄-alkyl group in the para position.
 10. The process according to claim 1, wherein for the compound of Formula I: M¹ is zirconium; R¹ and R² are identical and each is chlorine; R³ and R¹⁰ are identical or different and are selected from a methyl, ethyl, or isopropyl group; R⁴, R⁶, R⁷, R⁸, R¹¹, R¹³, R¹⁴, and R¹⁵ are each a hydrogen; R⁵ and R¹² are identical and are selected from a hydrogen or a p-t-butylphenyl group; and R⁹ is a bridge between the ligands, which is represented by the following formula:

whereby: M² is silicon; and R¹⁶ and R¹⁷ are each identical and are a methyl group.
 11. The process according to claim 1, wherein the compound of Formula I has a structure corresponding to one or more of the following:


12. The process according to claim 1, wherein the compound of Formula I has a structure corresponding to the following:


13. The process according to claim 1, wherein the compound of Formula I has a structure corresponding to the following:


14. The process according to claim 1, wherein the compound of Formula I has a structure corresponding to the following:


15. The process according to claim 1, wherein the compound of Formula I has a structure corresponding to the following:


16. The process according to claim 1, wherein the compound of Formula I has a structure corresponding to the following:


17. The process according to claim 1, wherein ethylene is reacted in the presence of the catalyst system to produce a polyethylene homopolymer.
 18. The process according to claim 1, wherein ethylene is reacted with additional olefin monomers in the presence of the catalyst system to produce a copolymer comprising predominantly ethylene monomers.
 19. The process according to claim 18, wherein the additional olefin monomers are characterized by having 3-20 carbon atoms.
 20. The process according to claim 18, wherein the additional olefin monomers are characterized by having 3-10 carbon atoms.
 21. The process according to claim 18, wherein the additional olefin monomers are selected from the group consisting of propene, butene, 1-pentene, 1- hexene, 1-decene, 4-methyl-1-pentene, 1-octene, styrene, 1,3-butadiene, 1,4-hexadiene, vinyl norbornene, norbornadiene, ethyl norbornadiene, norbornene, cyclopentadiene, tetracyclododecene, methylnorbornene, and combinations thereof.
 22. The process according to claim 18, wherein the additional olefin monomers include an alpha olefin having 3 to 8 carbon atoms.
 23. The process according to claim 21, wherein the olefin is selected from the group consisting of propene, butene, 1-pentene, 1-hexene, styrene, butadiene, and combinations thereof.
 24. The process according to claim 18, wherein the ethylene is co-polymerized with propene.
 25. The process according to claim 18, wherein the fraction of additional olefin monomers is 0.1 to 10 weight % of the total monomers reacted.
 26. The process according to claim 1, wherein the process produces a polymer having a viscosimetrically-determined molecular weight of greater than 1×10⁶ g/mol.
 27. The process according to claim 1, wherein the process produces a polymer having a molecular weight distribution M_(w)/M_(n) of from 2 to
 6. 28. The process according to claim 1, wherein the catalyst system contains at least one co-catalyst.
 29. The process according to claim 28, wherein the co-catalyst is a Lewis acid.
 30. The process according to claim 28, wherein the co-catalyst is an aluminoxane compound.
 31. The process according to claim 28, wherein the co-catalyst is a methylaluminoxane compound.
 32. The process according to claim 30, wherein the co-catalyst is present in the catalyst system in a molar ratio of aluminum to transition metal of 10:1 to 1000:1.
 33. The process according to claim 1, wherein the compound in Formula I is present in a supported form.
 34. A method of using a catalyst system to produce high, very high, and ultra-high molecular weight ethylene homopolymer or copolymers, wherein the method comprises reacting ethylene in the presence of said catalyst system to produce a polymer comprising predominantly ethylene monomers and having a viscosimetrically-determined molecular weight of at least 0.7×10⁶ g/mol, and wherein said catalyst system comprises: (i) at least one catalyst having the formula:

whereby: M¹ is a transition metal of the 4^(th) to 6^(th) group of the periodic table, wherein the oxidation level of said transition metal does not equal zero; R¹ is hydrogen or a C₁-C₂₀-carbonaceous group or a halogen atom; R² is hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom; R³ and R¹⁰ are each identical or different and are each a C₁-C₂₀ carbonaceous group; R⁴, R⁵, R⁶, R⁷, R⁸, R¹¹, R¹², R¹³, R¹⁴, and R¹⁵ are each identical or different and are each hydrogen or a halogen atom or a C₁-C₂₀ carbonaceous group, whereby, optionally, two or several consecutively form a cyclic system; and R⁹ is a bridge between the ligands, which is represented by one of the following formulas:

whereby: M² is either silicon, germanium or tin; and R¹⁶ and R¹⁷ are each identical or different and are each hydrogen or a C₁-C₂₀ carbonaceous group or a halogen atom; and (ii) at least one co-catalyst; with the proviso that when R⁵ or R¹² constitutes a phenyl group supporting an alkyl group, the alkyl group is present in a para position.
 35. A process of manufacturing high, very high, and ultra high molecular weight polymers comprising predominantly ethylene monomers, wherein the process comprises reacting ethylene in the presence of a catalyst system to produce a polymer having a viscosimetrically-determined molecular weight of at least 0.7×10⁶ g/mol, wherein the catalyst system comprises a bridged metallocene catalyst compound having a zirconium dichloride central functionality and a dimethyl silandiyl bridge between five-membered rings of the metallocene compound, and wherein the rings are indenyl groups, with the proviso that both rings are substituted at the 2-position with respect to the dimethyl silandiyl bridge with a C₁-C₂₀ carbonaceous group; with the proviso that when R⁵ or R¹² constitutes a phenyl group supporting an alkyl group, the alkyl group is present in a para position.
 36. The process according to claim 35, wherein at least one of the rings is substituted with a C₂-C₂₀ carbonaceous group at the 2-position with respect to the dimethyl silandiyl bridge.
 37. The process according to claim 35, wherein the reaction occurs at a temperature of from −20° C. to 300° C.
 38. The process according to claim 35, wherein the reaction occurs at a pressure of from 0.5 bar to 2000 bar. 